PA6-GF
PA6-GF LATAMID 6 H2 G30-V0AF
Manufacturer：Not recorded
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.66 | g/cm³ |
| Tensile strength | 130.0 | MPa |
| Tensile modulus | 11000.0 | MPa |
| Elongation at break | 2.0 | % |
| HDT 1.8MPa | 190.0 | °C |
| HDT 0.45MPa | 215.0 | °C |
| Vicat softening point | 210.0 | °C |
| Flame rating | {'gwfi': 960, 'gwfi_thickness_tested': '2 mm', 'gwit': 850, 'gwit_thickness_tested': '2 mm', 'ul_94_flame_rating': 'V-2', 'thickness_tested': '0.75 mm'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 90 - 100 °C; time 3 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 230 - 250 °C; mold temperature 70 - 100 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1