Copolymer
PA6+PA66_LATAMID 68 H2-V0H BLACK3319_S
Manufacturer：Not recorded
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Tensile strength | 60.0 | MPa |
| Tensile modulus | 3300.0 | MPa |
| Elongation at break | 20.0 | % |
| Notched impact strength | 4.0 | kJ/m² |
| HDT 1.8MPa | 60.0 | °C |
| HDT 0.45MPa | 163.0 | °C |
| Vicat softening point | 208.0 | °C |
| Flame rating | V-0 | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 80 - 100 °C; time 3 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 250 - 270 °C; mold temperature 70 - 90 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1