Elastomer modified polypropylene
TPO-MX10
Manufacturer：博雷利思
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 0.97 | g/cm³ |
| Melt flow rate | 9.0 | g/10min |
| Tensile strength | 18.0 | MPa |
| Tensile modulus | 1250.0 | MPa |
| Elongation at break | 80.0 | % |
| Flexural strength | 23.0 | MPa |
| Flexural modulus | 1300.0 | MPa |
| Notched impact strength | 50.0 | kJ/m² |
| HDT 1.8MPa | 49.0 | °C |
| HDT 0.45MPa | 92.0 | °C |
| Vicat softening point | 43.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 80 °C; time 2 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 220 - 260 °C; mold temperature 30 - 50 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1
- Application areas：page 1