IRPC
HI630
Manufacturer：普莱克斯
高冲击或冲击改性
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Melt flow rate | 6.5 | g/10min |
| Tensile strength | 25.5 | MPa |
| Flexural modulus | 2354.0 | MPa |
| Notched impact strength | 88.3 | kJ/m² |
| HDT 1.8MPa | 90.0 | °C |
| Vicat softening point | 95.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 180 - 240 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: electrical and electronics. Verify the source, exact use and applicable approvals.