矿物填充改性聚丙烯
PPcompound 8900P
Manufacturer：沙特基础工业公司
高流动、高刚度、高冲击、低收缩率、低线性热膨胀系数、UV稳定
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.08 | g/cm³ |
| Melt flow rate | 2.16 | g/10min |
| Tensile strength | 24.0 | MPa |
| Tensile modulus | 2600.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural modulus | 2300.0 | MPa |
| Notched impact strength | 3.5 | kJ/m² |
| HDT 1.8MPa | 130.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
Verified grade-specific storage, drying, equipment settings and application details are not available in this record. Request the latest processing guide and safety data sheet for this exact grade from the manufacturer before establishing production settings.
- Storage
- Confirm packaging, temperature and humidity, shelf life, and handling after opening.
- Drying
- Confirm whether drying is required, plus temperature, time, dew point and target moisture.
- Equipment setup
- Confirm barrel and mold temperatures, injection conditions, residence time, purging and safe shutdown.
- Applications
- Confirm the manufacturer’s intended processes, application limits and relevant approvals for this grade.