Polyphenylene Ether (PPE) + High Impact Polystyrene (HIPS)
PX9406P
Manufacturer：诺瑞尔
无人值守的电器应用，如PCB支架、端子块+连接器、电路保护/继电器/开关、电机端盖、控制箱/面板和电池充电器/保险丝夹
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.1 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 73.0 | MPa |
| Tensile modulus | 2600.0 | MPa |
| Elongation at break | 4.5 | % |
| Flexural modulus | 2500.0 | MPa |
| Notched impact strength | 11.0 | kJ/m² |
| HDT 1.8MPa | 117.0 | °C |
| Vicat softening point | 150.0 | °C |
| Flame rating | 5VA at 2.5mm and V0 at 0.75mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 105 - 110 °C; time 3 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 275 - 305 °C; mold temperature 70 - 100 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2