Flame retardant polypropylene homopolymer compound
PP-GF25 POLYFLAM® RPP 2000 E
Manufacturer：Not recorded
阻燃
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 0.91 | g/cm³ |
| Melt flow rate | 2.0 | g/10min |
| Tensile strength | 38.0 | MPa |
| Tensile modulus | 1900.0 | MPa |
| Elongation at break | 8.0 | % |
| Notched impact strength | 9.0 | kJ/m² |
| HDT 1.8MPa | 61.0 | °C |
| HDT 0.45MPa | 109.0 | °C |
| Vicat softening point | 97.0 | °C |
| Flame rating | V-2 class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 70 °C; time 4 - 6 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 190 - 205 °C; mold temperature 40 - 80 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1