Polypropylene (PP) with Glass Fiber Reinforcement
PP-GF10 Fiberfil® J-6910/E
Manufacturer：Not recorded
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 0.978 | g/cm³ |
| Melt flow rate | 9.0 | g/10min |
| Tensile strength | 62.1 | MPa |
| Tensile modulus | 4140.0 | MPa |
| Elongation at break | 3.5 | % |
| Flexural strength | 79.3 | MPa |
| Flexural modulus | 3100.0 | MPa |
| Notched impact strength | 48.0 | kJ/m² |
| HDT 1.8MPa | 154.0 | °C |
| HDT 0.45MPa | 143.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 210 - 232 °C; mold temperature 38 - 66 °C. Verify the source, grade and conditions.