PC (聚碳酸酯)
PC 1303HP-08
Manufacturer：LG化学
高冲击或冲击改性，紫外线稳定或耐候，透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 8.0 | g/10min |
| Tensile strength | 60.0 | MPa |
| Tensile modulus | 2410.0 | MPa |
| Elongation at break | 120.0 | % |
| Flexural strength | 96.0 | MPa |
| Flexural modulus | 2410.0 | MPa |
| Notched impact strength | 900.0 | kJ/m² |
| HDT 1.8MPa | 129.0 | °C |
| HDT 0.45MPa | 145.0 | °C |
| Vicat softening point | 151.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.