PC (聚碳酸酯)
L-1250Z 100
Manufacturer：帝人化学有限公司
紫外线稳定或耐候性，透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 8.0 | g/10min |
| Tensile strength | 61.0 | MPa |
| Tensile modulus | 2400.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural strength | 93.0 | MPa |
| Flexural modulus | 2350.0 | MPa |
| Notched impact strength | 76.0 | kJ/m² |
| HDT 1.8MPa | 129.0 | °C |
| HDT 0.45MPa | 142.0 | °C |
| Vicat softening point | 149.0 | °C |
| Flame rating | {'HB': 'class', 'V-2': 'class', 'GWFI': {'1.5 mm': 825, '3 mm': 875}, 'GWIT': {'1.5 mm': 850, '3 mm': 850}} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.