聚碳酸酯
K-1300Y
Manufacturer：潘力特
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 2.8 | g/10min |
| Tensile strength | 60.0 | MPa |
| Tensile modulus | 2350.0 | MPa |
| Elongation at break | 6.0 | % |
| Flexural strength | 90.0 | MPa |
| Flexural modulus | 2200.0 | MPa |
| Notched impact strength | 89.0 | kJ/m² |
| HDT 1.8MPa | 132.0 | °C |
| HDT 0.45MPa | 145.0 | °C |
| Vicat softening point | 151.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.