Polycarbonate (PC)
Makrolon® ET3227 RE
Manufacturer：科思创
紫外线稳定或耐候性
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 3.0 | g/10min |
| Tensile strength | 66.0 | MPa |
| Tensile modulus | 2400.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural strength | 100.0 | MPa |
| Flexural modulus | 2400.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 128.0 | °C |
| HDT 0.45MPa | 140.0 | °C |
| Vicat softening point | 146.0 | °C |
| Flame rating | {'HB_class': 'HB', 'oxygen_index': '28%', 'glow_wire_flammability_index': {'1.5_mm': '875°C', '3.0_mm': '960°C'}} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.