Polycarbonate
AX2477 ST
Manufacturer：Makrolon®
紫外线稳定，易于释放
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 20.0 | g/10min |
| Tensile strength | 66.0 | MPa |
| Tensile modulus | 2400.0 | MPa |
| Elongation at break | 6.0 | % |
| Flexural strength | 98.0 | MPa |
| Flexural modulus | 2350.0 | MPa |
| Notched impact strength | 65.0 | kJ/m² |
| HDT 1.8MPa | 124.0 | °C |
| HDT 0.45MPa | 136.0 | °C |
| Vicat softening point | 143.0 | °C |
| Flame rating | {'GWFI': '850 °C', 'thickness': '0.75 mm'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.