polycarbonate copolymer resin
ELCRIN™ HPX4B
Manufacturer：LNP
专用
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 58.0 | MPa |
| Tensile modulus | 2210.0 | MPa |
| Elongation at break | 5.8 | % |
| Flexural strength | 94.0 | MPa |
| Flexural modulus | 2210.0 | MPa |
| Notched impact strength | 65.0 | kJ/m² |
| HDT 1.8MPa | 124.0 | °C |
| Vicat softening point | 141.0 | °C |
| Flame rating | {'glow_wire_flammability_index': '825 °C', 'glow_wire_ignition_temperature': '825 °C', 'ul_94_flame_rating': 'HB', 'thickness_tested': '1.5 mm'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.