Polycarbonate (PC) Siloxane Copolymer
ELCRIN™ EXL9414B
Manufacturer：LNP™
中流动，无氯，无溴，阻燃，不透明，注塑级，生物来源成分
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 11.5 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2140.0 | MPa |
| Elongation at break | 5.6 | % |
| Flexural strength | 86.0 | MPa |
| Flexural modulus | 2180.0 | MPa |
| Notched impact strength | 29.0 | kJ/m² |
| HDT 1.8MPa | 117.0 | °C |
| HDT 0.45MPa | 131.0 | °C |
| Vicat softening point | 136.0 | °C |
| Flame rating | UL94 V0 @1.0mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.