polycarbonate (PC) siloxane copolymer resin
EXL9253RCC
Manufacturer：LNP™ ELCRIN™
阻燃，无卤，高冲击或冲击改性，紫外线稳定或耐候，不透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 15.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2190.0 | MPa |
| Elongation at break | 110.0 | % |
| Flexural strength | 87.0 | MPa |
| Flexural modulus | 2190.0 | MPa |
| Notched impact strength | 48.0 | kJ/m² |
| HDT 1.8MPa | 124.0 | °C |
| HDT 0.45MPa | 112.0 | °C |
| Vicat softening point | 128.0 | °C |
| Flame rating | UL94 V0 at 1.0mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.