siloxane copolymer resin
ELCRIN™ EXL7253RCC
Manufacturer：LNP™
紫外线稳定，中等流动，非氯化，非溴化，阻燃，不透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 12.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2260.0 | MPa |
| Elongation at break | 100.0 | % |
| Flexural strength | 86.0 | MPa |
| Flexural modulus | 2170.0 | MPa |
| Notched impact strength | 80.0 | kJ/m² |
| HDT 1.8MPa | 105.0 | °C |
| HDT 0.45MPa | 116.0 | °C |
| Vicat softening point | 123.0 | °C |
| Flame rating | UL94 V0 at 0.6mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.