polycarbonate (PC) siloxane copolymer resin
ELCRIN™ EXL1613TBL
Manufacturer：LNP™
有弹性的，共聚物
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.18 | g/cm³ |
| Melt flow rate | 8.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2100.0 | MPa |
| Elongation at break | 67.0 | % |
| Flexural strength | 85.0 | MPa |
| Flexural modulus | 2100.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 122.0 | °C |
| Vicat softening point | 142.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.