Polycarbonate (PC) siloxane copolymer
ELCRIN™ EXL1414B
Manufacturer：LNP™
韧性的，共聚物
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2150.0 | MPa |
| Elongation at break | 120.0 | % |
| Flexural strength | 85.0 | MPa |
| Flexural modulus | 2250.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 128.0 | °C |
| HDT 0.45MPa | 140.0 | °C |
| Vicat softening point | 145.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.