Polycarbonate copolymer
ELCRIN™ DMX6034RCC
Manufacturer：LNP™
耐磨
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.16 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 61.0 | MPa |
| Tensile modulus | 2070.0 | MPa |
| Elongation at break | 75.0 | % |
| Flexural strength | 2100.0 | MPa |
| Flexural modulus | 2120.0 | MPa |
| Notched impact strength | 40.0 | kJ/m² |
| HDT 1.8MPa | 131.0 | °C |
| HDT 0.45MPa | 117.0 | °C |
| Vicat softening point | 136.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.