Polycarbonate copolymer blend
ELCRES™ SLX1271D
Manufacturer：LNP™
耐候性，紫外线稳定
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.21 | g/cm³ |
| Melt flow rate | 18.0 | g/10min |
| Tensile strength | 66.0 | MPa |
| Tensile modulus | 2260.0 | MPa |
| Elongation at break | 115.0 | % |
| Flexural strength | 97.0 | MPa |
| Flexural modulus | 2250.0 | MPa |
| Notched impact strength | 7.0 | kJ/m² |
| HDT 1.8MPa | 123.0 | °C |
| HDT 0.45MPa | 134.0 | °C |
| Vicat softening point | 138.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.