Polycarbonate resin
ELCRES™ EXL9818
Manufacturer：LNP™
良好的加工性，良好的模量和耐热性，无氯无溴阻燃
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.21 | g/cm³ |
| Melt flow rate | 21.0 | g/10min |
| Tensile strength | 61.0 | MPa |
| Tensile modulus | 2520.0 | MPa |
| Elongation at break | 92.0 | % |
| Flexural strength | 90.0 | MPa |
| Flexural modulus | 2410.0 | MPa |
| Notched impact strength | 62.0 | kJ/m² |
| HDT 1.8MPa | 131.0 | °C |
| HDT 0.45MPa | 119.0 | °C |
| Vicat softening point | 138.0 | °C |
| Flame rating | 5VA/2.5mm, V0/1.5mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.