Polycarbonate (PC) siloxane copolymer resin
ELCRES™ EXL1414AML
Manufacturer：LNP™
高冲击或冲击改性，不透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 11.0 | g/10min |
| Tensile strength | 53.0 | MPa |
| Tensile modulus | 2070.0 | MPa |
| Elongation at break | 119.0 | % |
| Flexural strength | 73.0 | MPa |
| Flexural modulus | 2220.0 | MPa |
| Notched impact strength | 72.0 | kJ/m² |
| HDT 1.8MPa | 128.0 | °C |
| HDT 0.45MPa | 140.0 | °C |
| Vicat softening point | 140.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.