Polycarbonate
Copolymer XHT2141
Manufacturer：LEXAN™
高流动，高热
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 46.0 | g/10min |
| Tensile strength | 70.0 | MPa |
| Tensile modulus | 2600.0 | MPa |
| Elongation at break | 6.5 | % |
| Flexural modulus | 2450.0 | MPa |
| Notched impact strength | 12.0 | kJ/m² |
| HDT 1.8MPa | 155.0 | °C |
| HDT 0.45MPa | 145.0 | °C |
| Vicat softening point | 160.0 | °C |
| Flame rating | {'GWFI': 960, 'GWIT': 875, 'Vicat Temperature': 161, 'Burning behav. at 1.5 mm nom. thickn.': 'HB class'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.