Polycarbonate
Copolymer EXL9414T
Manufacturer：LEXAN™
阻燃，透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 13.0 | g/10min |
| Tensile strength | 59.0 | MPa |
| Tensile modulus | 2180.0 | MPa |
| Elongation at break | 124.0 | % |
| Flexural modulus | 2180.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 120.0 | °C |
| Vicat softening point | 138.0 | °C |
| Flame rating | UL-94 V0 | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.