PC
Copolymer EXL1494T
Manufacturer：LEXAN™
极低温度延展性，中等流动特性，改进的释放性，优良的加工性
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 59.0 | MPa |
| Tensile modulus | 2180.0 | MPa |
| Elongation at break | 124.0 | % |
| Flexural modulus | 2180.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 120.0 | °C |
| Vicat softening point | 138.0 | °C |
| Flame rating | {'class': 'V-2', 'thickness_tested': '3.0 mm', 'glow_wire_flammability_index': '960 °C', 'glow_wire_ignition_temperature': '850 °C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.