Polycarbonate (PC) siloxane copolymer resin
Copolymer EXL1463T
Manufacturer：LEXAN™
透明，注塑级，优异的低温延展性，中等流动性，改进的脱模性，优异的加工性
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2350.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural modulus | 2150.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 124.0 | °C |
| Vicat softening point | 141.0 | °C |
| Flame rating | {'HB class': None, 'V-2 class': None, 'Glow Wire Flammability Index (GWFI)': 960, 'Glow Wire Ignition Temperature (GWIT)': 825, 'GWIT - thickness tested (3 mm)': None} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.