PC
Copolymer EXL1434
Manufacturer：LEXAN™
中等流动度不透明注塑级，紫外线稳定
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 9.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2150.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural modulus | 2250.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 66.0 | °C |
| Vicat softening point | 145.0 | °C |
| Flame rating | {'vicat_temperature': 145, 'class': 'HB', 'glow_wire_flammability_index': 960, 'glow_wire_ignition_temperature_1mm': 875, 'glow_wire_ignition_temperature_3mm': 875} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.