PC
Copolymer EXL1414
Manufacturer：Not recorded
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2150.0 | MPa |
| Elongation at break | 6.0 | % |
| Flexural modulus | 2250.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| Vicat softening point | 145.0 | °C |
| Flame rating | {'vicat_softening_temperature_b': '145 °C', 'glow_wire_flammability_index_gwfi': '960 °C', 'glow_wire_ignition_temperature_gwit_1mm': '875 °C', 'glow_wire_ignition_temperature_gwit_3mm': '875 °C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.