PC
EXL1414H
Manufacturer：LEXAN™ 共聚物
不透明PC-硅氧烷共聚物，具有良好的加工性能。中等流动性，极低温度韧性。增强的耐水解稳定性。仅提供黑色。
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 57.0 | MPa |
| Tensile modulus | 2150.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural modulus | 2250.0 | MPa |
| Notched impact strength | 70.0 | kJ/m² |
| HDT 1.8MPa | 139.0 | °C |
| Vicat softening point | 145.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
Verified grade-specific storage, drying, equipment settings and application details are not available in this record. Request the latest processing guide and safety data sheet for this exact grade from the manufacturer before establishing production settings.
- Storage
- Confirm packaging, temperature and humidity, shelf life, and handling after opening.
- Drying
- Confirm whether drying is required, plus temperature, time, dew point and target moisture.
- Equipment setup
- Confirm barrel and mold temperatures, injection conditions, residence time, purging and safe shutdown.
- Applications
- Confirm the manufacturer’s intended processes, application limits and relevant approvals for this grade.
You may consult the family overview; it does not provide verified settings for this grade: Material-family guide