PC
Copolymer EXL1330
Manufacturer：LEXAN™
{'加工/物理特性': '熔体体积流动率，MVR：9 cm³/10min，熔体流动指数，MFI：10 g/10min', '机械性能': '拉伸模量：2100 MPa，屈服应力：55 MPa，屈服应变：5 %，断裂应力：56 MPa，断裂应变：50 %，弯曲模量：2100 MPa，冲击强度，+23°C，3mm：kJ/m²，缺口冲击强度，+23°C，3mm：75 kJ/m²，缺口冲击强度，-30°C，3mm：60 kJ/m²，Izod冲击强度，+23°C：kJ/m²，Izod缺口冲击强度，+23°C，3mm：70 k
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.18 | g/cm³ |
| Melt flow rate | 10.0 | g/10min |
| Tensile strength | 56.0 | MPa |
| Tensile modulus | 2100.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural modulus | 2100.0 | MPa |
| Notched impact strength | 75.0 | kJ/m² |
| HDT 1.8MPa | 134.0 | °C |
| HDT 0.45MPa | 120.0 | °C |
| Vicat softening point | 143.0 | °C |
| Flame rating | {'Vicat softening temperature, B': '143 °C', 'Vicat softening temperature, 120°C/h 50N': '145 °C', 'Burning behav. at thickness h': 'HB class', 'Glow Wire Flammability Index (GWFI)': '960 °C', 'Glow Wire Ignition Temperature (GWIT) - thickness tested (1)': '875 °C', 'Glow Wire Ignition Temperature (GWIT) - thickness tested (3)': '875 °C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 120 °C; time 3 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 295 - 315 °C; mold temperature 70 - 95 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2
- Application areas：page 2