PC
Copolymer EXL1112
Manufacturer：LEXAN™
{'Processing': '注塑成型', 'Applications': '汽车', 'Regional Availability': '北美'}
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.183 | g/cm³ |
| Melt flow rate | 16.0 | g/10min |
| Tensile strength | 527.0 | MPa |
| Tensile modulus | 527.0 | MPa |
| Elongation at break | 527.0 | % |
| Flexural modulus | 178.0 | MPa |
| Notched impact strength | 60.0 | kJ/m² |
| HDT 1.8MPa | 123.0 | °C |
| Vicat softening point | 145.0 | °C |
| Flame rating | {'Vicat softening temperature, B': '144 °C', 'Burning behav. at thickness h': 'HB class', 'Glow Wire Flammability Index (GWFI)': '960 °C', 'Glow Wire Ignition Temperature (GWIT) - thickness tested (1)': '875 °C', 'Glow Wire Ignition Temperature (GWIT) - thickness tested (3)': '875 °C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.