High Heat Polycarbonate Copolymer Resin
CXT19
Manufacturer：LEXAN™ 共聚物
190°C Vicat温度和透明度，优化以具有广泛的加工窗口和有限的黄色，有限透明色
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.22 | g/cm³ |
| Melt flow rate | 33.0 | g/10min |
| Tensile strength | 65.0 | MPa |
| Tensile modulus | 2600.0 | MPa |
| Elongation at break | 25.0 | % |
| Flexural modulus | 2600.0 | MPa |
| Notched impact strength | 9.0 | kJ/m² |
| HDT 1.8MPa | 185.0 | °C |
| HDT 0.45MPa | 190.0 | °C |
| Vicat softening point | 50.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.