Polycarbonate (PC) resin
Copolymer CFR7630 - Asia
Manufacturer：LEXAN™
非氯化，非溴化，阻燃，透明和半透明
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 5.0 | g/10min |
| Tensile strength | 68.0 | MPa |
| Tensile modulus | 2500.0 | MPa |
| Elongation at break | 51.0 | % |
| Flexural strength | 52.0 | MPa |
| Flexural modulus | 2400.0 | MPa |
| Notched impact strength | 10.0 | kJ/m² |
| HDT 1.8MPa | 131.0 | °C |
| HDT 0.45MPa | 120.0 | °C |
| Vicat softening point | 139.0 | °C |
| Flame rating | UL-94 V0 rating at 1.0 mm, 5VA rating at 3.0mm, UV stabilized (F1 rating) | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.